| Thermosetting acrylic resin | |||||||||
| Series No | Appearance | Solid Content (%) | Viscosity s, 25¡æ (Gardner) | Color Fe-Co (¡Ü) | Hydroxy value (Supply) (mgKOH/g) | Acid value MgKOH/g | Solvent | Characteristics | Uses |
| BS-8160 | Water white Or light yellow transparent liquid | 60¡À2 | 40-60 | 1 | 70 | 2-5 | Xylene, CAC Butyl acetate | High gloss and hardness, good distinctness of image, quick drying, good adhesion to metal, good application | Automotive-refinishing paint, varnish, and solid paint |
| BS-8170-A | 70¡À2 | 40-70 | 1 | 70 | 10-12 | Xylene, Propylene glycol methyl ether acetate | Good fullness, quick drying, high hardness, excellent weather resistance, good application | Automotive -refinishing paint, motorcycle paint, Plastic paint | |
| BS-9570-C | 70¡À2 | 50-70 | 1 | 80 | 6-8 | Xylene,CAC Butyl acetate | El0 modified PU polyol acrylic resin with high gloss, fullness and distinctness of image, excellent gasoline resistance, good gloss retention | Automotive -refinishing paint, motorcycle paint and finishing varnish | |
| BS9570-E | 70¡À2 | 25-45 | 1 | 70 | 9-12 | Xylene, Propylene glycol methyl ether acetate | El0 modified PU polyol acrylic resin, quick-drying, high hardness, high-gloss, good gloss retention | Automotive and motorcyele paint, finishing varnish, combined with curing agent | |
| BS-8060 | 60¡À2 | 50-75 | 1 | 70 | 2-4 | Xylene, Propylene glycol methyl ether acetate | High gloss and hardness, good disrinctness of image, quick-drying, broad compatibility with alkyd resin,excellent yellowing resistance and rubbingproperty,good scratch resistance, | Finish coat, finish and primer for wood paint, combined with TDI curing agent | |
| BS-8061 | 60¡À2 | 70-90 | 1 | 60 | 12-14 | Xylene, Butyl acetate | Good fullness, color and gloss retention, good flatting effect, and adhesion to metal(such as stainless steel) | Matt finish for wood paint, metal finish, combined with curing agent | |
| BS-8070 | 70¡À2 | 30-50 | 1 | 70 | 6-8 | Xylene, S-100# | High solid content, high fullness and gloss, excellent yellowing resistance | Finish coat, finish etc, for high-grade wood paint, such as finish coat for piano and plastic | |
| BS-8011 | 60¡À2 | 30-60 | 1 | 60 | 8-10 | Xylene, CAC | High gloss, good distinctness of image, quick-drying, good water resistance, excellent physical property | Used for auto-repairing paint | |
| BS-8155 | 55¡À2 | 20-35 | 1 | 27 | 9-11 | Toluene | Quick-drying, good adhesion, high hardness, clear hammer pattern, good hammer tone effect | Hammer tone paint, used for painting Machine tool and engineering machine, combined with curing agent | |
| BS-9460 | 60¡À2 | 45-80 | 1 | 36 | 4-7 | Xylene, Butyl acetate | Excellent aluminum powder orientation, good metal adhesion, broad compatibility with CAB, quick-drying and high hardness | Automotive-refinishing paint, metallic paint, and solid paint, combined with curing agent | |
| BS-8170 | 70¡À2 | 35-60 | 1 | 70 | 10-12 | Xylene, Propylene glycol methyl ether acetate | High solid content, fullness, distinctness of image | Automotive-refinishing paint, Motorcycle paint, plastics paint, solid finish, and finishing coat, combined with curing agent | |
| BS-9570 | 70¡À2 | 70-110 | 1 | 80 | 7-10 | Xylene, Propylene glycol methyl ether acetate | E10 modified PU polyol acrylic resin, high solid content, excellent fullness and distinctness of image, gasoline resistance, and high hardness | Automotive-refinishing paint, Motorcycle paint, solid finish, and finishing coat, combined with curing agent | |
| BS-8270 | 70¡À2 | 55-80 | 1 | 100 | 10-12 | Xylene, Propylene glycol methyl ether acetate | High hydroxyl and solid content, excellent weather resistance, chemical resistance, good fullness and gasoline resistance | Automotive-refinishing paint, Motorcycle paint, solid finish, and finishing coat, combined with curing agent | |
| BS-8160 | Water white Or light yellow transparent liquid | 60¡À2 | 40-60 | 1 | 70 | 2-5 | Xylene,CAC Butyl acetate | High gloss and hardness, good distinctness of image, quick drying, good adhesion to metal, good application | Automotive-refinishing paint, varnish, and solid paint |
| BS-8170-A | 70¡À2 | 40-70 | 1 | 70 | 10-12 | Xylene,Propylene Glycol methyl Ether acetate | Good fullness, quick drying, high hardness, excellent weather resistance, good application | Automotive -refinishing paint, motorcycle paint, Plastic paint | |
| BS-9570-C | 70¡À2 | 50-70 | 1 | 80 | 6-8 | Xylene,CAC Butyl acetate | El0 modified PU polyol acrylic resin with high gloss, fullness and distinctness of image, excellent gasoline resistance, good gloss retention | Automotive -refinishing paint, motorcycle paint and finishing varnish | |
| BS9570-E | 70¡À2 | 25-45 | 1 | 70 | 9-12 | Xylene,Propylene Glycol methyl Ether acetate | El0 modified PU polyol acrylic resin, quick-drying, high hardness, high-gloss, good gloss retention | Automotive and motorcyele paint, finishing varnish, combined with curing agent | |
| BS-8060 | 60¡À2 | 50-75 | 1 | 70 | 2-4 | Xylene,Propylene Glycol methyl Ether acetate | High gloss and hardness, good disrinctness of image, quick-drying, broad compatibility with alkyd resin,excellent yellowing resistance and rubbing property,good scratch resistance, | Finish coat, finish and primer for wood paint, combined with TDI curing agent | |
| BS-8061 | 60¡À2 | 70-90 | 1 | 60 | 12-14 | Xylene, Butyl acetate | Good fullness, color and gloss retention, good flatting effect, and adhesion to metal(such as stainless steel) | Matt finish for wood paint, metal finish, combined with curing agent | |
| BS-8070 | 70¡À2 | 30-50 | 1 | 70 | 6-8 | Xylene, S-100# | High solid content, high fullness and gloss, excellent yellowing resistance | Finish coat, finish etc, for high-grade wood paint, such as finish coat for piano and plastic | |
| BS-8011 | 60¡À2 | 30-60 | 1 | 60 | 8-10 | Xylene, CAC | High gloss, good distinctness of image, quick-drying, good water resistance, excellent physical property | Used for auto-repairing paint | |
| BS-8155 | 55¡À2 | 20-35 | 1 | 27 | 9-11 | Toluene | Quick-drying, good adhesion, high hardness, clear hammer pattern, good hammer tone effect | Hammer tone paint, used for painting Machine tool and engineering machine, combined with curing agent | |
| BS-9460 | 60¡À2 | 45-80 | 1 | 36 | 4-7 | Xylene,Butyl acetate | Excellent aluminum powder orientation, good metal adhesion, broad compatibility with CAB, quick-drying and high hardness | Automotive-refinishing paint, metallic paint, and solid paint, combined with curing agent | |
| BS-8170 | 70¡À2 | 35-60 | 1 | 70 | 10-12 | Xylene,Propylene Glycol methyl Ether acetate | High solid content, fullness, distinctness of image | Automotive-refinishing paint, Motorcycle paint, plastics paint, solid finish, and finishing coat, combined with curing agent | |
| BS-9570 | 70¡À2 | 70-110 | 1 | 80 | 7-10 | Xylene,Propylene Glycol methyl Ether acetate | El0 modified PU polyol acrylic resin, high solid content, excellent fullness and distinctness of image, gasoline resistance, and high hardness | Automotive-refinishing paint, Motorcycle paint, solid finish, and finishing coat, combined with curing agent | |
| BS-8270 | 70¡À2 | 55-80 | 1 | 100 | 10-12 | Xylene,Propylene Glycol methyl Ether acetate | High hydroxyl and solid content, excellent weather resistance, chemical resistance, good fullness and gasoline resistance | Automotive-refinishing paint, Motorcycle paint, solid finish, and finishing coat, combined with curing agent | |
| BS-9770 | Water white Or light yellow transparent liquid | 70¡À2 | 30-60 | 1 | 60 | 8-10 | Xylene, Propylene Glycol methyl ether acetate | High solid content, good fullness, excellent distinctness of image, good weather resistance, high gloss | OEM automotive paint, solid finish, finishing coat, combined with amino resin |
| BS-9970 | 70¡À2 | 40-60 | 1 | 65 | 8-10 | Xylene, Propylene Glycol methyl ether acetate | High fullness, excellent resistance to weather, good gloss and color retention | OEM automotive paint, solid finish, finishing coat, combined with amino resin | |
| BS-8260 | 60¡À2 | 15-25 | 1 | 55 | 5-6 | Xylene, Butyl acetate | Excellent aluminum powder orientation, simultaneously compatibility with amino, CAB and epoxy, good adhesion and excellent weather resistance | Painting for vehicle surface, electrical appliance's coating, finish, metallic paint, primer and intermediate coating, combined with amino resin | |
| BS-9360 | 60¡À2 | 15-25 | 1 | 60 | 8-11 | Xylene | Excellent adhesion to aluminum or galvanized sheet, high hardness and gloss, and excellent wetting and dispersion of pigment, good gasoline resistance | Finish coat, solid paint and metallic paint, combined with amino resin | |
| BS-9760 | 60¡À2 | 40-70 | 1 | 60 | 70-80 | Ethylene glycol butyl ether, n-Butand | Water-based and oil-based, high hardness, good mar-resistance and adhesion to copper and glass etc | Used for lamp decoration, glass paint, galvaniging article finishing, waterborne amino baking paint, combined with amino resin | |
| BS-9060 | 60¡À2 | 75-110 | 1 | 60 | 5-8 | Xylene, Butyl acetate | Excellent aluminum powder orientation effect, big molecular weight, big viscosity, quick drying, good flexibility and impact resistance, excellent combinedphysical properties | Aluminum paint for machine hull, universal baking paint | |
| BS-961 | Water white Or light yellow transparent liquid | 50¡À2 | 70-150 (Tu-Cup4) | 1 | 81.8¡À3.3 | 12 | -5 | Xylene,Butanol | Together with amino resin to produce amino acrylic baking paint, paint film is quick-drying, and shows high gloss, high fullness and good combinedproperties | Automobile, agricultural machinery vehicle, domestic appliance, metal print, bicycle etc |
| BS-961-3 | 50¡À2 | 120-170 (Tu-Cup4) | 1 | 81.8¡À3.3 | 12 | -5 | Xylene,Butanol | Amino acrylic baking paint, paint film shows a high gloss, high fullness and good combined properties. | Automobile, agricultural machinery vehicle, domestic appliance, bicycle etc | |
| BS-962 | 50¡À2 | 60-150 (Tu-Cup4) | 1 | 70¡À3.3 | 10 | 30.8 | Xylene | Together with aliphatic urethane curing agent to produce acrylic urethane paint, which shows excellent weather resistance and "three-resistance"property* | High-grade automobile paint tile-like paint or painting for export product etc | |
| BS-963 | 50¡À2 | 60-160 (Tu-Cup4) | 1 | 48.2¡À3.3 | 10 | 27.3 | Xylene | Acrylic urethane paint, paint film shows good combined properties and excellent "three-resistance¡± property* | Automobile, agricultural machinery vehicle, domestic appliance, railway vehicle, along with tile-like coating etc | |
| BS-965 | 65¡À2 | 35-65 (Gradner-Holdt Tube) | 1 | 85.8¡À3.3 | 10 | 15.8 | Xylene,Butyl Acetate | Together with 3880 polyester to produce gloss polyester paint; together with N-75 and N3390 to produce automotive paint; together with amino resin to produce baking paint; high quality, low cost | Maybe employed for gloss polyester furniture paint, flooring paint, automotive paint, and motorcycle paint, etc multiple use | |
| BS-965-2U | 65¡À2 | 35-65 (Gradner-Holdt Tube) | 1 | 85.8¡À3.3 | 6 | 15.6 | Xylene,Butyl Acetate,S-150 | Together with 3880 polyester to produce gloss polyester paint; together with N-75 and N3390 to produce automotive paint; together with amino resin to produce baking paint; high quality, low cost. Gel time of the paint vehicle is extended when combined with curing agent | Gloss polyester furniture paint, may be also mixed with amino resin to make baking paint and used in motorcyle and aluminum paint etc | |
| BS-965-3 | 65¡À2 | 50-90 (Gradner-Holdt Tube) | 1 | 85.8¡À3.3 | 3 | 15.6 | Xylene,Butyl Acetate | High solid and low acid value; used as aluminum paint; together with aliphatic urethane curing agent or amino resin to produce air-drying paint or baking paint | Aluminum paint and metallic paint for mortorcycle or industrial use | |
| BS-965-5 | 65¡À2 | 70-110 (Gradner-Holdt Tube) | 1 | 85.8¡À3.3 | 9 | 15.8 | Xylene,Butyl Acetate | High solid content and high viscosity; may be mixed with aliphatics or aromatics curing agent, the paint film shows a high gloss, fullness and hardness, a goodwearability and good feeling, and low cost | Gloss polyester furniture paint, may be mixed with a definite amount of 3880 saturated polyester for the sake of increase fullness | |
| BS-965-10 | 65¡À2 | 35-65 (Gradner-Holdt Tube) | 1 | 87¡À3.3 | 10 | 16 | Xylene,Butyl Acetate | Together with combined with aliphatic urethane curing agent to produce acrylic urethane paint, the paint film shows a high fullness, high gloss and hardness, sometimes it may be also mixed with aromatic curing agent to produce furniture finish, or with amino resin to produce baking paint | Automobile, agricultural machinery vehicle, domestic appliance etc, when used in mortorcycle paint, it show the best effect | |
| BS-966 | 50¡À2 | 50-100 (Tu-Cup4) | 1 | 91.7¡À3.3 | 2 | -32 | Toluene | Very low acid value and Tg; may be mixed with urethane curing agent (aliphatics or aromatics), the paint film shows a good flexibility and impact resistance. | Used in aluminum metal or used as aluminum paint, metallic paint and used in leather, metal print as well | |
| BS-969 | 60¡À2 | 8-15 (Gradner-Holdt Tube) | 1 | 44.9¡À3.3 | 10 | 27.8 | Xylene, Ethoxyethyl Acetate | Acrylic urethane paint, and paint film shows high gloss and fullness, good distinctness of image and combined properties, excellent higher "three-resistance property* and decoration | Automobile agricultural machinery vehicle, domestic appliance etc | |
| Series No | Appearance | Solid Content (%) | Viscosity s, 25¡æ (Gardner) | Color Fe-Co (¡Ü) | Hydroxy value(Calculated) mgKOH/g | Acid value MgKOH/g | Tg¡æ | Solvent | Characteristics | Uses |
| BS-961 | Water white Or light yellow transparent liquid | 50¡À2 | 70-150 (Tu-Cup4) | 1 | 81.8¡À3.3 | 12 | -5 | Xylene,Butanol | Together with amino resin to produce amino acrylic baking paint, paint film is quick-drying, and shows high gloss, high fullness and good combinedproperties | Automobile, agricultural machinery vehicle, domestic appliance, metal print, bicycle etc |
| BS-961-3 | 50¡À2 | 120-170 (Tu-Cup4) | 1 | 81.8¡À3.3 | 12 | -5 | Xylene,Butanol | Amino acrylic baking paint, paint film shows a high gloss, high fullness and good combined properties. | Automobile, agricultural machinery vehicle, domestic appliance, bicycle etc | |
| BS-962 | 50¡À2 | 60-150 (Tu-Cup4) | 1 | 70¡À3.3 | 10 | 30.8 | Xylene | Together with aliphatic urethane curing agent to produce acrylic urethane paint, which shows excellent weather resistance and "three-resistance"property* | High-grade automobile paint tile-like paint or painting for export product etc | |
| BS-963 | 50¡À2 | 60-160 (Tu-Cup4) | 1 | 48.2¡À3.3 | 10 | 27.3 | Xylene | Acrylic urethane paint, paint film shows good combined properties and excellent "three-resistance¡± property* | Automobile, agricultural machinery vehicle, domestic appliance, railway vehicle, along with tile-like coating etc | |
| BS-965 | 65¡À2 | 35-65 (Gradner-Holdt Tube) | 1 | 85.8¡À3.3 | 10 | 15.8 | Xylene,Butyl Acetate | Together with 3880 polyester to produce gloss polyester paint; together with N-75 and N3390 to produce automotive paint; together with amino resin to produce baking paint; high quality, low cost | Maybe employed for gloss polyester furniture paint, flooring paint, automotive paint, and motorcycle paint, etc multiple use | |
| BS-965-2U | 65¡À2 | 35-65 (Gradner-Holdt Tube) | 1 | 85.8¡À3.3 | 6 | 15.6 | Xylene,Butyl Acetate,S-150 | Together with 3880 polyester to produce gloss polyester paint; together with N-75 and N3390 to produce automotive paint; together with amino resin to produce baking paint; high quality, low cost. Gel time of the paint vehicle is extended when combined with curing agent | Gloss polyester furniture paint, may be also mixed with amino resin to make baking paint and used in motorcyle and aluminum paint etc | |
| BS-965-3 | 65¡À2 | 50-90 (Gradner-Holdt Tube) | 1 | 85.8¡À3.3 | 3 | 15.6 | Xylene,Butyl Acetate | High solid and low acid value; used as aluminum paint; together with aliphatic urethane curing agent or amino resin to produce air-drying paint or baking paint | Aluminum paint and metallic paint for mortorcycle or industrial use | |
| BS-965-5 | 65¡À2 | 70-110 (Gradner-Holdt Tube) | 1 | 85.8¡À3.3 | 9 | 15.8 | Xylene,Butyl Acetate | High solid content and high viscosity; may be mixed with aliphatics or aromatics curing agent, the paint film shows a high gloss, fullness and hardness, a goodwearability and good feeling, and low cost | Gloss polyester furniture paint, may be mixed with a definite amount of 3880 saturated polyester for the sake of increase fullness | |
| BS-965-10 | 65¡À2 | 35-65 (Gradner-Holdt Tube) | 1 | 87¡À3.3 | 10 | 16 | Xylene,Butyl Acetate | Together with combined with aliphatic urethane curing agent to produce acrylic urethane paint, the paint film shows a high fullness, high gloss and hardness, sometimes it may be also mixed with aromatic curing agent to produce furniture finish, or with amino resin to produce baking paint | Automobile, agricultural machinery vehicle, domestic appliance etc, when used in mortorcycle paint, it show the best effect | |
| BS-966 | 50¡À2 | 50-100 (Tu-Cup4) | 1 | 91.7¡À3.3 | 2 | -32 | Toluene | Very low acid value and Tg; may be mixed with urethane curing agent (aliphatics or aromatics), the paint film shows a good flexibility and impact resistance. | Used in aluminum metal or used as aluminum paint, metallic paint and used in leather, metal print as well | |
| BS-969 | 60¡À2 | 8-15 (Gradner-Holdt Tube) | 1 | 44.9¡À3.3 | 10 | 27.8 | Xylene, Ethoxyethyl Acetate | Acrylic urethane paint, and paint film shows high gloss and fullness, good distinctness of image and combined properties, excellent higher "three-resistance property* and decoration | Automobile agricultural machinery vehicle, domestic appliance etc | |
| BS-970 | Water white Or light yellow transparent liquid | 50¡À2 | 100-160 (Tu-Cup4) | 1 | 39.6¡À3.3 | 12 | 16 | Toluene | May be mixed with urethane paint, curing agent to produce air-drying paint, and used as well as amino baking paint as well | Specially for hammer tone paint |
| BS-960 | 60¡À2 | 30-55 (Gradner-Holdt Tube) | 1 | 85.8¡À3.3 | 6 | 16 | Xylene, Butyl acetate | May be mixed with urethane curing agent to produce gloss polyester paint; the paint film shows high gloss and hardness, good wearability and feeling (mixing with 3880 to increase the paint film's fullness), add amino resin to produce baking paint | Gloss polyester furniture paint or industry baking paint | |
| BS-960U | 60¡À2 | 50-100 | 1 | 90¡À3.3 | 3 | 14 | Butanol | Together with combined with aliphatic urethane curing agent to produce acrylic urethane paint, good aluminum powder orientation, good paint filmappearamce | Aluminum paint for mortorcycle or industrial use | |
| BS-960-2U | 60¡À2 | 50-100 | 1 | 90¡À3.3 | 3 | 14 | Xylene, | low acid value, together with amino resin to produce aluminum paint, good aluminum powder orientation, good paint film appearamce, lower cost | Aluminum paint for motorcycle or industrial use | |
| BS-960-4U | 60¡À2 | 60-90 | 1 | 90¡À3.3 | 3 | 40 | Butyl alcohol | The resin is low acid value, together with amino resin to produce aluminum paint, good aluminum powder orientation, good paint film appearamce,higher Tg, high hardness | Aluminum paint for mortorcycle or industrial use | |
| BS-960P | 60¡À2 | 35-65 | 1 | 87¡À3.3 | 9 | 15 | Butyl acetate S-100A | Together with aromatics urethane curing agent to produce environmentally friendly gloss furniture paint, paint film shows a good hardness, good gloss and feeling, a good wearability | Belong to environmentally friendly resin, may be produce automobile, and motorcycle or paint or industrial use and baking paint combined with amino resin | |
| BS-985 | 50¡À2 | 10-18 (Gardner) | 1 | 39.6¡À3.3 | 12 | 29.9 | Xylene | Pure acrylic resin with low hydroxyl content; cure with N-75 and N3390; excellent weather resistance and "three-resistance"property*; is a high-grade paint with economy | Automobile,,agricultural machinery vehicle, domestic appliance, along with high-grade tile-like paint, and exterior industrial coating | |
| BS-987-1 | 50¡À2 | 140-210 (Tu-Cup4) | 1 | 76.9¡À3.3 | 3 | 4.6 | Xylene | Low acid value; cure with N-75 and N3390 to produce aluminum paint and metallic paint and the paint film shows good combined properties, add amino resin to produce baking paint | Automobile, along with industrial aluminum paint, metallic paint,(self cure paint for especial use) | |
| BS-988-2 | 55¡À2 | ¡Ý450 (Tu-Cup4) | 1 | 88¡À3.3 | 10 | -15 | Xylene, Butanol | Amino acrylic baking paint with high viscosity and solid content; the paint film shows good combined properties | Special steel tape paint, paint for coil coated aluminium | |
| BS-991 | 55¡À2 | 4-8 (Gardner) | 1 | 160¡À3.3 | 10 | 30.5 | Xylene | Acrylic resin with high hydroxyl content | Semi product of silicone modified acrylic resin (high-temperature resistant paint) react with silicone to produce silicone modified acrylic resin | |
| BS-9960 | 60¡À2 | 40-100 (Gardner) | 1 | 87.8¡À3.3 | 8 | 15.2 | Xylene, Butyl acetate | Pure acrylic resin, outstanding yellowing resistance, and excellent "three-resistance"property*; it is mixed with aliphatic curing agent | Automobile, agricultural machinery vehicle, domestic appliance etc | |
| BS-9202-1 | Water white Or light yellow transparent liquid | 60¡À2 | 8-16 (Gardner) | 1 | 99¡À3.3 | 10 | 60 | Xylene,Butyl acetate, Propylene glycol methyl ether acetate | Very high gloss, paint film shows a high gloss and fullness and hardness and good decoration; cured by aliphatic curing agent | High-grade automotive paint, and acrylic urethane paint for motorcycle |
| BS-982U | 60¡À2 | 8-15 (Gardner) | 1 | 115¡À3.3 | 10 | -32 | Xylene, Butyl acetate | Very low Tg, may be mixed with Solutia 747 or 717 to produce baking paint; which shows very good flexibility and impact resistance | Amino baking paint for export glove of artificial leather | |
| BS-982-3 | 60¡À2 | 10-20 (Gardner) | 1 | 109¡À3.3 | 10 | -26 | Xylene, Butyl acetate | Very low Tg, may be mixed with urethane uring agent; very good flexibility, adhesion and impact resistance | Paint for leather, glass and metal print, along with industrial paint with requirement of good impact resistance | |
| BS-965-F | 65¡À2 | 35-65 (Gardner) | 1 | 87¡À3.3 | 9 | 15 | Butyl acetate, S-100A | The resin without benzene used for environmentally-friendly paint, high solid content; may be with aromatic curing agent to produce gloss furniture finish; the paint film shows good hardness and gloss, good feeling and wearability; economic resin | May be mixed with a!iphatic curing agent to produce gloss polyester automotive paint; (may be mixed with a definite amount of 3880 polyester in order to increase fullness); amino paint for motorcycle etc when mixed with amino resin |