| Thermoplastic acrylic resin | |||||||||
| Series No | Appearance | Solid Content (%) | Viscosity s, 25¡æ (Gardner) | Color (¡Ü) | Acid value (mgKOH/g) | Tg(¡æ) | Solvent | Characteristics | Uses |
| BS-101 | Water white or light yellow transparent liquid | 50¡À2 | 6-16 | / | 8 | 8 | Toluene, Butyl acetate | Low Tg, used together with high Tg acrylic resin to increase the gloss and weather resistance |
Modified perchlorovinyl resin used as paint, transfer ink and correction liquor for writing also, or used as paint together with BS-102/BS-108 |
| BS-102 | 50¡À2 | 10-16 | / | 8 | 57.2 | Toluene | Quick-drying, high hardness, paint film has a high gloss and fullness, used together with low Tg acrylic resin |
Used together with 101 to produce modified perchlorovinyl paint, or used as floor paint alone |
|
| BS-103 | 59¡À2 | 10-20 | 1 | 12 | -19 | Toluene | Low Tg, used as acrylic modified nitrocellulose lacquer |
The paint film shows better combined property than that of alkyd medified nitrocellulose lacquer, quick-drying, used as matte furniture finish, automotive paint etc |
|
| BS-104 | 40¡À2 | 120-140 (Tu-Cup4) | 1 | 12 | 32 | Toluene, Butyl acetate | Quick-drying, better weather resistance, water resistance, and three-resistance property* |
High-grade exterior wall coating, road marking paint etc. |
|
| BS-104-2 | 50¡À2 | 8-16 | 1 | 10 | 29 | Toluene | Quick-drying, good water resistance and adhesion. |
Road marking paint |
|
| BS-105 | 50¡À2 | 180-280(Tu-Cup4) | 1 | 12 | 32 | Toluene | One component quick-drying paint, paint film shows high gloss and fullness, excel lent weather resistance |
Used together with BS-108 for agricultural automobile, electrical appliance or engineering machine paint etc |
|
| BS-105-1 | 50¡À2 | 180-280(Tu-Cup4) | 1 | 3 | 32 | Toluene | Low acid value, One component, used as quick-drying aluminum paint. |
Motor paint, aluminum paint for industrial use |
|
| BS-108 | 50¡À2 | 8-16 | 1 | 10 | 58 | Toluene, Butyl acetate | One component quick-drying paint, paint film shows high hardness, gloss and fullness, good combined properties |
Used together with BS-105 for motor paint or industrial finish, or used as container paint by itself |
|
| BS-109 | 50¡À2 | 100-280(Tu-Cup4) | / | 3 | 41 | Toluene | Low acid value, paint film is quick-drying good gloss, good combined property, toughness |
Specially for air spray painting |
|
| BS-109-60 | 60¡À2 | 8-12 | / | 3 | 39 | Toluene, Butyl acetate | Low acid value, paint film is quick-drying and good gloss, high fullness, good combined property, toughness |
Specially for air spray painting |
|
| BS-121 | 50¡À2 | 7-16 | 1 | 10 | 37 | Xylene, Butyl acetate | One-component quick-drying pure acrylic coating, may be used together with BS-1996, the paint film shows high gloss and fullness, excellent weather resistance and three-resistance property* |
Used together with BS1996 to produce high-grade exterior wall paint, road marking paint encaustic tile paint and automotive finish |
|
| BS-116 | 50¡À2 | 180-280(Tu-Cup4) | 1 | 12 | 55 | Toluene, Butyl acetate | Quick-drying, higher hardness and water resistance |
Typically universal exterior wall paint |
|
| BS-121-3F | Water white or light yellow transparent liquid | 50¡À2 | 20-55 | 1 | 12 | 39.1 | Ethyl acetate, S-100A | Environmentally-friendly paint with micro benzene, air-drying, quick-drying, good flame retardancy, water resistance, and light-fastness | Super-thin fire-retardant coating for steel structure |
| BS-1201A | 50¡À2 | 20-40 | 1 | 3 | 90 | Toluene, Butanol | Paint film shows high gloss, hardness and fullness, quick-drying, excellent combined property | Specially forABS plastic paint, may be used as aluminum paint or gloss paint low cost | |
| BS-1201¼× | 45¡À2 | 20-40 | 1 | 2 | 88 | Toluene, Butanol | Low acid value, good aluminum powder orientation, good miscibility with NC or CAB, quick-drying high application property, alcohol resistance, scrub resitance used as a high-grade ABS paint | High-grade ABS aluminum paint, semi-gloss or matte solid paint, used in TV cover, stereo system etc | |
| BS-1201Îì | 45¡À2 | 20-35 | 1 | 2 | 90 | Toluene, Butyl acetate | Low acid value, may be used as aluminum paint, matte paint or semi gloss paint; quick-drying, alcohol-resistance, scrub-resistance and migration resistance | Specially for ABS plastic paint, high-grade aluminum paint for TV or stereo system etc, metal-like paint | |
| BS-1201F | 50¡À2 | 30-70 | 1 | 3 | 60 | Ethyl acetate, Isobutanol, Isopropanol | Used for soft PVC paint film, which is quick-drying, has a good adhesion, high gloss and good flexibility | Used in soft PVC film | |
| BS1201¼º | 50¡À2 | 30-70 | 1 | 10 | 52 | Toluene, Butyl acetate | Quick-drying, paint film shows light-gloss, good adhesion, high hardness, fair combined properties for hard PVC material | Use in hard PVC special resin | |
| BS1201X | 50¡À2 | 10-20 | 1 | 10 | 60 | n-Butyl Alcohol, Dipropyl ketone Alcohol, Butyl acetate | Good adhesion to polystyrene substrate, paint film shows brightness and fullness, quick-drying, high hardness, good combined properties | Special resin for polystyrene substrate | |
| BS1201E | 50¡À2 | 10-20 | 1 | 12 | 42.4 | Xylene S-100A | Good adhesion to weave bag, paint film shows brightness and fullness, high-grade water resistance and humidity resistance | Special resin for weave bag, economic type resin | |
| BS-1209 | 50¡À2 | 15-25 | 1 | 3 | 44 | Toluene | Low acid value, may be used as quick-drying aluminum paint; the paint film shows a high hardness, good adhesion and good flexibility,low cost | Aluminum paint specially for agricnltural automobile, quick-drying aluminum paint or solid finish | |
| BS-1966 | 50¡À2 | 11-25 | 1 | 10 | 58.3 | Xylene | Paint film is quick-drying, and has goo three-resistance property* | Used for container paint | |
| BS-1996 | 50¡À2 | 24-65 | 1 | 8 | 56 | Xylene | Excellent three-resistance property*, yellowig and water resistance, higher hardness | May be mixed with proper amout of BS-120 to make high grade exterior wall paint, encaustic tile paint or road marking paint | |
| BS-113 | 50¡À2 | 5000-10000cps | 1 | 15 | 44 | Toluene, Butyl acetate | Quick-drying, high hardness, easy rubbing | Putty or used in wainscot | |
| BS2350 | Water white Or light Yellow Transparent | 50¡À2 | 30-50 | 1 | 2-4 | 42 | Xylene, Butyl acetate | Low hydroxy, hydroxy content1.8%, single-package or two component, excellent adhesion to plastic and metal, Extensive compatibility with CAB, cellulosenitrate, good flexibility and weather resistance, | Automotive refinishing paint, plastics paint, may be also used as universal colour paste |
| BS2460 | Liquid | 60¡À2 | 40-60 | 1 | 5-8 | 30 | Xylene, Butyl acetate | Compatibility with CAB cellulose nitrate, good flexibility, excellent adhesion to metal | Used in engineering machine, anticorrosive paint |
| BS-1604 | Light yellow Opaque liquid | 40¡À2 | 70-110 (Tu-Cup4) | 1 | 6-8 | 65 | Xylene | Excellent adhesion to PP or OPP, excellent aluminum powder orientation | Paint for auto-bumper bar and washing machine's exterior body, PP, OPP coating, metallic paint, solid paint and finish coat |
| BS-1650 | Water white or light yellow transparent liquid | 50¡À2 | 20-45 | 1 | 2-4 | 88 | Xylene, Isobutanol | Excellent alcohol resistance, excellent aluminum powder orientation and adhesion to ABS | Plastic paint |
| BS-2040-A | 50¡À2 | 15-30 | 1 | 6-9 | 40 | Xylene | Excellent adhesion to glass or metal, good compatibility with cellulose nitrate | Glass paint, metal painting | |
| BS-2050 | 50¡À2 | 50-80 | 1 | 5-7 | 50 | Toluene, Xylene | Good flexibility, good dispersion for pigment, color and gloss retention, good chemical and alkali resistance | Used in engineering machine as anticorrosion of steel structure, exterior wall paint, paint for rattan articles | |
| BS-2060 | 50¡À2 | 35-60 | 1 | 1.5-3 | 60 | Loluene, Isobutanol | Quick-drying, compatibility with various materials, excellent aluminum powder orientation, good adhesion to ABS, PS, HIPS etc, and may be diluted by alcoholsolvent | Toy coating, plastic paint | |
| BS-2092 | 50¡À2 | 40-60 | 1 | 2-3 | 92 | Toluene, Isobutanol | High gloss and hardness, excellent aluminum powder orientation, good adhesion to ABS, PS, HIPS, and may be diluted by alcohol solvent | Toy coating, plastic paint | |
| BS2150 | 50¡À2 | 25-50 | 1 | 3-5 | 50 | xylene | Low hydroxy, hydroxy content 1.1 %, single-package excellent adhesion to plastic and metal, Extensive compatibility with CAB, good chemical and weatherresistance | Ship paint for plastic, engineering machine, ship container, heavy duty anticorrosion automotive refinishing and motorcycle, universal colour paste | |