| Alkyd resin used for polyester paint application (common type) | ||||||||||
| Series No | Oil type | Oil length% (Reference) | Solid content% | Viscosity (cps/30¡æ) | Color (Fe-Co)# | Acid value (mgKOH/g) | Hydroxyl value (Caculated) MgKOH/g | Solvent | Characteristics | Uses |
| 1170D | Soya-bean fatty acid | 34 | 70¡À2 | 25000-50000 | ¡Ü2.5 | ¡Ü12 | 125 | Xylene Toluene | Good drying and easy wearability, good flexibility and impact resistance, Light color |
Polyester primer and matte finish |
| 1170F | Soya-bean fatty acid | 34 | 70¡À2 | 50000-80000 | ¡Ü2.5 | ¡Ü12 | 125 | Xylene Toluene | High molecular weight, quick-drying, good abrasion and flexibility, light color |
Quick-drying polyester primer |
| 3370F | Ricinolic acid | 34 | 70¡À2 | 25000-50000 | ¡Ü3.5 | ¡Ü10 | 125 | Xylene Butyl acetate | Quick-drying, good fullness, excellent matting agent orientation and deglossing prop erty |
Common matte finish, transparent primer and putty |
| 3801-70 | Oya-bean fatty acid | 34 | 70¡À2 | 10000-25000(25¡æ) | ¡Ü2 | ¡Ü10 | 120 | Xylene Butyl acetate | Quick-drying, good fullness,excellent matting agent orientation and deglossing property |
High grade matte finish or making high grade quick-dryingmatte finish together with quick drying curing agent |
| 3735-70 | Soya-bean fatty acid | 35 | 70¡À2 | 25000-50000 | ¡Ü2.5 | ¡Ü10 | 130 | Xylene Toluene | Quick-drying, good fullness, fair heat resistance, flexibility, good matting agent orientation |
High grade matte finish |
| 3738-70 | Soya-bean fatty acid | 35 | 70¡À2 | 25000-50000 | ¡Ü2.5 | ¡Ü15 | 140 | Xylene Toluene | Good drying, high hardness, easy rubbing, good adhesion |
High grade quick-drying transparent primer |
| 12-70A | Synthetic fatty acid | 30 | 70¡À2 | 15000-30000 | ¡Ü1 | ¡Ü12 | 140 | Xylene Toluene | Water white, high hardness, yellowing resistance, good brushing, high fullness |
High grade bright polyester finish and hand-brushing paint |
| 12-70B | Synthetic fatty acid | 30 | 70¡À2 | 15000-30000 | ¡Ü1 | ¡Ü10 | 100 | Xylene Toluene | Water white, moderate molecular weight, good leveling property, easy brushing, high hardness, good fullness and yellowing resistance |
High grade bright wood finish |
| 3880 | Synthetic fatty acid | 28 | 80¡À2 | 15000-30000 | ¡Ü1 | ¡Ü10 | 145 | Xylene Toluene | Water white, super high fullness and gloss, high hardness, excellent yellowing resistance |
Generally, mixed with BS960 to make highgrade crystal floor paint and high grade polyester paint |
| 3370C | Mixed fatty acid | 34 | 70¡À2 | 10000-25000 | ¡Ü2 | ¡Ü10 | 125 | Xylene Toluene | Light color, good fullness, high hardness and gloss |
Bright polyester finish |
| 3370D | Mixed fatty acid | 34 | 70¡À2 | 25000-50000 | ¡Ü2.5 | ¡Ü12 | 125 | Xylene Toluene | Light color, high hardness, easy rubbing, quick drying |
Matte polyester finish, primer, putty |
| 3670 | Ricinolic acid | 44 | 70¡À2 | 1000-2000 | ¡Ü2.5 | ¡Ü10 | 100(Exclusive of the contention oil) | Xylene Toluene | Light color, good brushing, fullness and flexibility, good impact resistance and adhesion |
Bright polyester hand-brushing paint |
| 3818-70D | Synthetic fatty acid | 35 | 70¡À2 | 25000-50000(30¡æ) | ¡Ü3 | ¡Ü12 | 100 | Xylene | Good drying, quick rubbing,excellent wettability and dispersibity forpigment |
High-grade two-component polyester primer and conventional matte paint |
| 3860¡Á70 | Soya-bean fatty acid | 35 | 70¡À2 | ¡Ý50000 | ¡Ü3 | ¡Ü12 | 95 | Xylene Toluene | Quick-drying, use a little amount of curing agent, good rubbing |
Polyester primer |